Loctite 430 1oz Metal Bonding Instant Adhesive

Loctite 430 1oz Metal Bonding Instant Adhesive

• Shear Strength, Grit Blasted Steel : 3600 psi
• Temperature : -65 - 180 °F
• Viscosity : 70 - 110 mPa.s (cP) Brookfield
• Key Substrates : Metals , Rubbers and Plastics
• Color : Clear
• Curing Type : Humidity
• Application : Bonding

 

LOCTITE® 430 is a transparent, colorless, methyl cyanoacrylate liquid general purpose adhesive and is particularly suited to bonding of metal substrates. It has been qualified to Commercial Item Description A-A-3097 (this is a regional approval).

• Low viscosity
• Particularly suited to bonding of metal substrates
• Qualified to Commercial Item Description A-A-3097 (this is a regional approval)

 
LOCTITE®
430™ is a general purpose adhesive and is
particularly suited to bonding of metal substrates.

Commercial Item Description A-A-3097:

LOCTITE®
430™ has been qualified to Commercial Item
Description A-A-3097. Note: This is a regional approval.
Please contact your local Technical Service Center for more
information and clarification.

TYPICAL CURING PERFORMANCE

Under normal conditions, the atmospheric moisture initiates the
curing process. Although full functional strength is developed
in a relatively short time, curing continues for at least 24 hours
before full chemical/solvent resistance is developed.

Cure Speed vs. Substrate

The rate of cure will depend on the substrate used. The table
below shows the fixture time achieved on different materials
at 22 °C / 50 % relative humidity. This is defined as the time to
develop a shear strength of 0.1 N/mm².

Cure Speed vs. Bond Gap

The rate of cure will depend on the bondline gap. Thin bond
lines result in high cure speeds, increasing the bond gap will
decrease the rate of cure.

Cure Speed vs. Humidity

The rate of cure will depend on the ambient relative humidity.
The following graph shows the tensile strength developed with
time on Buna N rubber at different levels of humidity.

Cure Speed vs. Activator

Where cure speed is unacceptably long due to large gaps,
applying activator to the surface will improve cure speed.
However, this can reduce ultimate strength of the bond and
therefore testing is recommended to confirm effect.

GENERAL INFORMATION

This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials.
For safe handling information on this product, consult the
Safety Data Sheet (SDS).

Directions for use:

1. For best performance bond surfaces should be clean and
   free from grease.
2. This product performs best in thin bond gaps (0.05 mm).
3. Excess adhesive can be dissolved with Loctite cleanup
   solvents, nitromethane or acetone.

Loctite Material Specification

LMS dated September-1, 1995. Test reports for each batch
are available for the indicated properties. LMS test reports
include selected QC test parameters considered appropriate to
specifications for customer use. Additionally, comprehensive
controls are in place to assure product quality and
consistency. Special customer specification requirements may
be coordinated through Henkel Quality.

Storage

Store product in the unopened container in a dry location.
Storage information may be indicated on the product container
labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or
greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during
use. Do not return product to the original container. Henkel
Corporation cannot assume responsibility for product which
has been contaminated or stored under conditions other than
those previously indicated. If additional information is required,
please contact your local Technical Service Center or
Customer Service Representative.